Influence of Temporary Cements on the Bond Strength of Self-Adhesive Cement to the Metal Coronal Substrate

This research evaluated the influence of temporary cements (eugenol-containing [EC] or eugenol-free [EF]) on the tensile strength of Ni-Cr copings fixed with self-adhesive resin cement to the metal coronal substrate. Thirty-six temporary crowns were divided into 4 groups (n=9) according to the temporary cements: Provy, Dentsply (eugenol-containing), Temp Cem, Vigodent (eugenol-containing), RelyX Temp NE, 3M ESPE (eugenol-free) and Temp Bond NE, Kerr Corp (eugenol-free). After 24 h of temporary cementation, tensile strength tests were performed in a universal testing machine at a crosshead speed of 0.5 mm/min and 1 kN (100 kgf) load cell. Afterwards, the cast metal cores were cleaned by scraping with curettes and air jet. Thirty-six Ni-Cr copings were cemented to the cast metal cores with self-adhesive resin cement (RelyX U200, 3M ESPE). Tensile strength tests were performed again. In the temporary cementation, Temp Bond NE (12.91±2.54) and Temp Cem (12.22±2.96) presented the highest values of tensile strength and were statistically similar to each other (p>0.05). Statistically significant difference (p<0.05) was observed only between Provy (164.44±31.23) and Temp Bond NE (88.48±21.83) after cementation of Ni-Cr copings with self-adhesive resin cement. In addition, Temp Cem (120.68±48.27) and RelyX Temp NE (103.04±26.09) showed intermediate tensile strength values. In conclusion, the Provy eugenol-containing temporary cement was associated with the highest bond strength among the resin cements when Ni-Cr copings were cemented to cast metal cores. However, the eugenol cannot be considered a determining factor in increased bond strength, since the other tested cements (1 eugenol-containing and 2 eugenol-free) were similar.

Resumo Esta pesquisa avaliou a influência dos cimentos temporários (contendo eugenol [CE]ou livre de eugenol[LE]) na resistência à tração de copingsde Ni-Cr fixados com cimento resinoso auto-adesivo sobre substrato coronário metálico. Trinta e seis coroas provisórias foram divididas em 4 grupos (n=9) de acordo com os cimentos temporários: Provy, Dentsply (contendo eugenol), Temp Cem, Vigodent (contendo eugenol), RelyXTemp NE, 3M ESPE (livre de eugenol) andTemp Bond NE, KerrCorp (livre de eugenol). Após 24 h da cimentação temporária, testes de resistência à tração foram realizados em uma máquina universal de ensaios, com velocidade de 0,5 mm/min. e célula de carga de 1kN (100 kgf). Em seguida, os núcleos metálicos fundidos foram limpos por meio de raspagem com cureta ejatos de ar. Trinta e seis copings de Ni-Cr foram cimentados sobre os núcleos metálicos com cimento resinoso auto-adesivo (RelyX U200, 3M ESPE). Testes de resistência à tração foram novamente realizados. Na cimentação provisória, Temp Bond NE (12,91±2,54) e Temp Cem (12,22±2,96) apresentaram os maiores valores de resistência à tração e foram estatisticamente semelhantes entre si (p>0,05). Diferença estatisticamente significante (p<0.05) foi observada apenas entre Provy (164,44±31,23) e Temp Bond NE (88,48±21,83)após cimentação dos copingsdeNi-Cr com cimento resinoso auto-adesivo. Além disso, Temp Cem (120,68±48,27) e RelyX Temp NE (103,04±26,09) mostraram valores intermediários de resistência à tração. Em conclusão, o cimento temporário contendo eugenol, Proxy, foi associado com a mais alta resistência de união do cimento resinoso, quando os copingsde Ni-Cr foram cimentados sobre os núcleos metálicos fundidos. Entretanto, o eugenol não pode ser considerado como um fator determinante no aumento da resistência de união, já que outros cimentos testados (1 contendo eugenol e 2 livres de eugenol) foram semelhantes.

Influence of Temporary Cements on the Bond Strength of Self-Adhesive Cement to the Metal Coronal Substrate.

This research evaluated the influence of temporary cements (eugenol-containing [EC] or eugenol-free [EF]) on the tensile strength of Ni-Cr copings fixed with self-adhesive resin cement to the metal coronal substrate. Thirty-six temporary crowns were divided into 4 groups (n=9) according to the temporary cements: Provy, Dentsply (eugenol-containing), Temp Cem, Vigodent (eugenol-containing), RelyX Temp NE, 3M ESPE (eugenol-free) and Temp Bond NE, Kerr Corp (eugenol-free). After 24 h of temporary cementation, tensile strength tests were performed in a universal testing machine at a crosshead speed of 0.5 mm/min and 1 kN (100 kgf) load cell. Afterwards, the cast metal cores were cleaned by scraping with curettes and air jet. Thirty-six Ni-Cr copings were cemented to the cast metal cores with self-adhesive resin cement (RelyX U200, 3M ESPE). Tensile strength tests were performed again. In the temporary cementation, Temp Bond NE (12.91 ± 2.54) and Temp Cem (12.22 ± 2.96) presented the highest values of tensile strength and were statistically similar to each other (p>0.05). Statistically significant difference (p<0.05) was observed only between Provy (164.44 ± 31.23) and Temp Bond NE (88.48 ± 21.83) after cementation of Ni-Cr copings with self-adhesive resin cement. In addition, Temp Cem (120.68 ± 48.27) and RelyX Temp NE (103.04 ± 26.09) showed intermediate tensile strength values. In conclusion, the Provy eugenol-containing temporary cement was associated with the highest bond strength among the resin cements when Ni-Cr copings were cemented to cast metal cores. However, the eugenol cannot be considered a determining factor in increased bond strength, since the other tested cements (1 eugenol-containing and 2 eugenol-free) were similar.

Ultraconservative fixed partial denture: esthetic and preservation of dental structure / Prótese parcial fixa ultraconservadora: estética com preservação de estrutura dental

The oral rehabilitation can be made with several ways with the objective to reestablish the masticatory function and the esthetic of the patient. The aim of this clinical case is to present a different type of fixed partial denture, as alternative option to the dental surgeon, showing particularities like indications, contraindications, advantages, disadvantages and technical procedures necessary to its fabrication. The sequential presentation of the realized procedures emphasized the unique aspects of the dental preparation, impression techniques, and cautions during metal structures and ceramic try-in procedures, and esthetic overlay on the metal with composite resin. As a result, it could be observed that the ultraconservative fixed partial denture required lesser removal dental structure, re-established the esthetic and the occlusion of the patient. Finally, it can be concluded that the ultraconservative fixed partial denture is a treatment option to be used in the small prosthetic space with success both mechanically and esthetically.

A reabilitação oral pode ser realizada de diversas formas com o intuito de restabelecer a função mastigatória e a estética do paciente. Este caso clínico tem o objetivo de apresentar um tipo diferente de prótese parcial fixa, como opção alternativa para o cirurgião-dentista, mostrando suas particularidades quanto à indicação, contraindicação, vantagens, desvantagens e procedimentos necessários à sua elaboração. A apresentação sequencial dos procedimentos realizados ressaltou os aspectos únicos do preparo dental, da técnica de moldagem, dos cuidados a serem observados na prova da estrutura metálica, na prova da cerâmica, dos aspectos diferenciais na cimentação e do recobrimento estético da estrutura metálica com resina composta. Como resultado pode-se observar que a prótese ultraconservadora exigiu menor desgaste estrutural dos dentes pilares, restabeleceu a estética e a oclusão do indivíduo. Diante disso, pode-se concluir que a prótese parcial fixa ultraconservadora é uma opção de tratamento a ser utilizada em pequenos espaços protéticos com sucesso mecânico e estético.

Effect of temperature variation on the cytotoxicity of cast dental alloys and commercially pure titanium.

UNLABELLED: Cell culture system has been used to evaluate alloy cytotoxicity under different environments, testing the extracts, but the effect of temperature variation on the cytotoxicity of dental alloys has not been analyzed. OBJECTIVE: The aim of the present study was to investigate if temperature variation could affect dental alloy cytotoxicity, testing alloy extracts in an epithelial cell culture system. MATERIAL AND METHODS: Discs of Ni-Cr, Co-Cr-Mo, Ni-Cr-Ti, Ti-6Al-4V and commercially pure titanium (cp Ti) were cast by arc melting, under argon atmosphere, injected by vacuum-pressure. Discs were immersed in artificial saliva and subjected to different temperatures: 37 degrees C and thermocycling (37 degrees C/5 degrees C/37 degrees C/55 degrees C/37 degrees C). After thermocycling, extracts were put in a subconfluent culture during 6 h, and the number of cells and their viability were used to evaluate cytotoxicity in these temperatures. For each alloy, data from temperature conditions were compared by Student's t-test (alpha=0.05). RESULTS: The cytotoxicity tests with alloy/metal extracts showed that Ni-Cr, Co-Cr-Mo, Ti-6Al-4V and cp Ti extracts (p>0.05) did not affect cell number or cell viability, while Ni-Cr-Ti (p<0.05) extract decreased cell number and viability when the alloy was subjected to thermocycling. CONCLUSION: Within the limitations of the present study, the Ni-Cr-Ti alloy had cell number and viability decreased when subjected to temperature variation, while the other alloys/metal extracts did not show these results.

Effect of temperature variation on the cytotoxicity of cast dental alloys and commercially pure titanium

Cell culture system has been used to evaluate alloy cytotoxicity under different environments, testing the extracts, but the effect of temperature variation on the cytotoxicity of dental alloys has not been analyzed. OBJECTIVE: The aim of the present study was to investigate if temperature variation could affect dental alloy cytotoxicity, testing alloy extracts in an epithelial cell culture system. MATERIAL AND METHODS: Discs of Ni-Cr, Co-Cr-Mo, Ni-Cr-Ti, Ti-6Al-4V and commercially pure titanium (cp Ti) were cast by arc melting, under argon atmosphere, injected by vacuum-pressure. Discs were immersed in artificial saliva and subjected to different temperatures: 37ºC and thermocycling (37ºC/5ºC/37ºC/55ºC/37ºC). After thermocycling, extracts were put in a subconfluent culture during 6 h, and the number of cells and their viability were used to evaluate cytotoxicity in these temperatures. For each alloy, data from temperature conditions were compared by Student's t-test (α=0.05). RESULTS: The cytotoxicity tests with alloy/metal extracts showed that Ni-Cr, Co-Cr-Mo, Ti-6Al-4V and cp Ti extracts (p>0.05) did not affect cell number or cell viability, while Ni-Cr-Ti (p<0.05) extract decreased cell number and viability when the alloy was subjected to thermocycling. CONCLUSION: Within the limitations of the present study, the Ni-Cr-Ti alloy had cell number and viability decreased when subjected to temperature variation, while the other alloys/metal extracts did not show these results.

Comparative study of chemical and mechanical retentive systems for bonding of indirect composite resin to commercially pure titanium.

This study evaluated the effect of chemical and mechanical surface treatments for cast metal alloys on the bond strength of an indirect composite resin (Artglass) to commercially pure titanium (cpTi). Thirty cylindrical metal rods (3 mm diameter x 60 mm long) were cast in grade-1 cpTi and randomly assigned to 6 groups (n=5) according to the received surface treatment: sandblasting; chemical treatment; mechanical treatment - 0.4 mm beads; mechanical treatment - 0.6 mm beads; chemical/mechanical treatment - 0.4 mm; and chemical/mechanical treatment - 0.6 mm beads. Artglass rings (6.0 mm diameter x 2.0 mm thick) were light cured around the cpTi rods, according manufacturer's specifications. The specimens were invested in hard gypsum and their bond strength (in MPa) to the rods was measured at fracture with a universal testing machine at a crosshead speed of 2.0 mm/min and 500 kgf load cell. Data were analyzed statistically by one-way ANOVA and Tukey test (alpha=5%). The surface treatments differed significantly from each other (p<0.05) regarding the recorded bond strengths. Chemical retention and sandblasting showed statistically similar results to each other (p=0.139) and both had significantly lower bond strengths (p<0.05) than the other treatments. In conclusion, mechanical retention, either associated or not to chemical treatment, provided higher bond strength of the indirect composite resin to cpTi.

Tensile bond strength of cast commercially pure titanium and cast gold-alloy posts and cores cemented with two luting agents.

STATEMENT OF PROBLEM: In vitro studies on the retentive strengths of various cements used to retain posts have reported conflicting results. PURPOSE: The purpose of this study was to compare the tensile strength of commercially pure titanium and type III cast gold-alloy posts and cores cemented with zinc phosphate or resin cement. MATERIAL AND METHODS: Forty-two extracted human canines were endodontically treated. The root preparations were accomplished using Largo reamers (10 mm in depth and 1.7 mm in diameter). Acrylic resin patterns for the posts and cores were made, and specimens were cast in commercially pure titanium and in type III gold alloy (n=7). Fourteen titanium cast posts and cores were submitted to surface treatment with Kroll acid solution and to scanning electron microscopy (SEM), before and after acid etching. The groups (n=7) were cemented with zinc phosphate cement or resin cement (Panavia F). Tensile strengths were measured in a universal testing machine at a crosshead speed of 0.5 mm/min. The results (Kgf) were statistically analyzed by 2-way ANOVA (alpha=.05). RESULTS: The 2-way ANOVA indicated that there were no significant differences among the groups tested. Retentive means for zinc phosphate and Panavia F cements were statistically similar. The bond strength was not influenced by the alloy, the luting material, or the etching treatment. SEM analysis indicated that the etched surfaces were smoother than those that did not receive surface treatment, but this fact did not influence the results. CONCLUSIONS: Commercially pure titanium cast posts and cores cemented with zinc phosphate and resin cements demonstrated similar mean tensile retentive values. Retentive values were also similar to mean values recorded for cast gold-alloy posts and cores cemented with zinc phosphate cement and resin cements.

Comparative study of chemical and mechanical retentive systems for bonding of indirect composite resin to commercially pure titanium

This study evaluated the effect of chemical and mechanical surface treatments for cast metal alloys on the bond strength of an indirect composite resin (Artglass) to commercially pure titanium (cpTi). Thirty cylindrical metal rods (3 mm diameter x 60 mm long) were cast in grade-1 cpTi and randomly assigned to 6 groups (n=5) according to the received surface treatment: sandblasting; chemical treatment; mechanical treatment - 0.4 mm beads; mechanical treatment - 0.6 mm beads; chemical/mechanical treatment - 0.4 mm; and chemical/mechanical treatment - 0.6 mm beads. Artglass rings (6.0 mm diameter x 2.0 mm thick) were light cured around the cpTi rods, according manufacturer's specifications. The specimens were invested in hard gypsum and their bond strength (in MPa) to the rods was measured at fracture with a universal testing machine at a crosshead speed of 2.0 mm/min and 500 kgf load cell. Data were analyzed statistically by one-way ANOVA and Tukey test (a=5 percent). The surface treatments differed significantly from each other (p<0.05) regarding the recorded bond strengths. Chemical retention and sandblasting showed statistically similar results to each other (p=0.139) and both had significantly lower bond strengths (p<0.05) than the other treatments. In conclusion, mechanical retention, either associated or not to chemical treatment, provided higher bond strength of the indirect composite resin to cpTi.

Este estudo avaliou o efeito de tratamentos de superfície químico e mecânico para ligas metálicas fundidas sobre a resistência de união de uma resina composta indireta (Artglass) ao titânio comercialmente puro (Ti cp). Trinta varetas cilíndricas metálicas (3 mm diâmetro x 60 mm comprimento) foram fundidas em Ti cp grau 1 e igualmente divididas em grupos de acordo com os seguintes tratamentos de superfície: jateamento, químico, mecânico com esferas de 0,4 mm, mecânico com esferas de 0,6 mm, químico/mecânico com esferas de 0,4 mm e químico/mecânico com esferas de 0,6 mm. Anéis de Artglass (6 mm diâmetro X 2 mm espessura) foram fotopolimerizados ao redor das varetas, de acordo com as recomendações do fabricante. Os corpos-de-prova foram embutidos em gesso-pedra e a resistência de união (MPa) foi medida em uma máquina universal de ensaios com velocidade de 2,0 mm/min e célula de carga de 500 kgf. Os dados foram analisados estatisticamente por ANOVA a um critério e teste de Tukey (a=5 por cento). Houve diferença estatisticamente significante (p<0,05) entre os tratamentos de superfície quanto à resistência adesiva. Retenção química e jateamento apresentaram resultados estatisticamente semelhantes (p=0,139), e ambos apresentaram menores valores de retenção que os demais tratamentos (p<0,05). Em conclusão, a retenção mecânica, associada ou não a tratamento químico, apresentou melhores resultados de resistência adesiva do compósito indireto ao Ti cp.

Efeito do tratamento superficial da cerâmica sobre a força de união da resina composta / Effect of surface treatment on the shear bond strengths of the composite resin

Introdução: O alto potencial de fratura da cerâmica odontológica pode comprometer o resultado de uma reabilitação estética. O reparo intra-oral de uma cerâmica fraturada é muitas vezes uma alternativa viável para se evitar a remoção de uma prótese. A utilização de resina composta para esse tipo de reparo é uma das técnicas mais difundidas, mas, para que ocorra sucesso, é importante que seja garantida uma boa adesão entre a resina composta e a cerâmica, o que exige um preparo superficial da cerâmica. Este trabalho tem como objetivo avaliar a resistência de união de uma resina composta híbrida à superfície da cerâmica condicionada por diferentes tratamentos mecânico-químicos. Métodos: Foram confeccionados noventa discos de cerâmica (10x2mm) que foram incluídos em anel de PVC com resina acrílica e divididos em 3 grupos. Um grupo foi considerado grupo-controle (sem tratamento mecânico); trinta discos foram jateados com óxido de alumínio 50μm e trinta foram asperizados com ponta diamantada. Esses grupos foram subdivididos e submetidos aos tratamentos químicos: ácido fosfórico 35%, fluorfosfato de sódio acidulado 1,23% e ácido hidrofluorídrico 9,6%. Sobre a superfície tratada foi aplicada uma camada de silano e confeccionadas as restaurações em resina composta (5mm de diâmetro). Os corpos de provaforam termociclados e realizados testes de cisalhamento com célula de carga de 50 kgf e velocidade de 2mm/minuto. Resultados e conmclusão: Os resultados demonstraram que os tratamentos mecânico-químicos estudados são indicados para o reparo intra-oral de uma restauração cerâmica fraturada.

Introduction: High ceramic fracture rates may compromise the result of an esthetic rehabilitation. An intra-oral repair of fractured porcelain is may times a more cost-effective clinical method for avoiding a prosthesis removal. The clinical success of the ceramic repair method is dependent on the integrity of the bond between the porcelain repair and the composite resin. This integrity is achieved either by chemical or mechanical bonds. The objective of this study is to evaluate, in vitro, the bond strength of a composite resin to porcelain after different mechanical and chemical treatments. Methods: Ninety porcelain disks (10mm in diameter and 2mm thick) were prepared in a Teflon die and embedded in acrylic resin. Two groups were abraded with mechanical treatments: micro-etcher using Al2O3 particles or abraded with diamond burs. One group served as a control. These disks were submitted to a chemical treatment: 35% phosphoric acid; 1.23% acidulated phosphate fluoride and 9.6% hydrofluoridric acid. The composite resin restoration was made after the application of silane. The samples were thermocycled and the bond strength was determined using a testing machine at a cross-head of 2mm/min with a 50 kgf load-cell. Results and conclusion: The results indicated that the mechanical and chemical treatments studied are indicated to repair fractured porcelain.

Influêcia de agentes isolantes na retenção de cimentos temporários / Influence of insulating agents in temporary cements retention

O objetivo deste estudo foi avaliar a ação de três agentes isolantes aplicados sobre a superfície de núcleos metálicos fundidos para a confecção de coroas provisórias e a sua influência na fixação com diferentes agentes cimentantes temporários. A partir de uma matriz foram confeccionados 45 padrões em resina acrílica autopolimerizável (Duralay), fundidos com liga de cobre-alumínio (Novelli) e divididos em 9 grupos (n=5). Os núcleos foram isolados com saliva artificial (grupo controle), gel aquoso à base de glicerina (K-Y®) ou vaselina pastosa (Rioquímica), e a seguir confeccionadas as coroas provisórias em resina acrílica autopolimerizável (Vipiflash). Os núcleos eram posicionados em um dispositivo e realizada a cimentação das coroas, com carga padronizada de 300g, com os cimentos Dycal, Provicol e Temp bond. Removidos os excessos, as amostras foram armazenadas em água destilada a 37°C por 40 horas; após esse período foi realizado o ensaio de tração em uma máquina universal EMIC-DL2000 (velocidade = 5mm/minuto e célula de carga = 50 Kgf). A análise de variância evidenciou diferenças estatisticamente significantes para os fatores individuais (p≤0,0l) e para a interação (p≤0,05). Os testes complementares de Tukey e Scheffé indicaram diferenças entre os três agentes isolantes (saliva=8,73; K-Y®= 7,03 e Vaselina= 6,26) e para os cimentos a diferença entre o par formado por Temp Bond/Dycal e Provicol, respectivamente 8.47, 7.60 e 5.95 Kgf. Pelos resultados conclui-se que a saliva deve ser o agente isolante usado na confecção de coroas provisórias a serem cimentadas com Dycal ou Temp bond.

Análise comparativa da profundidade de fratura de dentes restaurados com núcleos metálicos fundidos ou núcleos de fibra de carbono / Comparative analysis of the depth of fracture of teeth restored with cast metal post and core and carbon fiber posts

Os núcleos metálicos fundidos são muito empregados para a restauração de dentes tratados endodonticamente, mas ultimamente tem havido um crescente interesse pelos sistemas de pinos pré-fabricados, como os de fibra de carbono, que é um material com boas propriedades físicas e mecânicas. O objetivo deste trabalho foi fazer uma comparação, através de ensaios de compressão, esses dois sistemas, tendo-se como grupo controle dentes tratados endodonticamente sem pinos. Concluiu-se que o núcleo metálico fundido provocou fraturas mais profundas, dificultando a restauração dos dentes envolvidos, e que os núcleos de fibra de carbono pareceram oferecer maiores possibilidades de reparo clínico

Núcleos de preenchimento em resina composta: uma opçäo viável / Composite resin used for posts and core: a practicable choice

Para a restauraçäo de dentes tratados endodonticamente alguns tipos de sistemas säo necessários para se conseguir retençäo suficiente para uma coroa ou prótese fixa. Os métodos mais difundidos säo os pinos fundidos ou pré-fabricados. Recentemente, materiais restauradores como a amálgama, cimentos de ionômero de vidro ou resina composta têm sido indicados como núcleos de preenchimento, diminuindo o custo do tratamento. Este trabalho relata um caso clínico de restauraçäo de um dente incisivo lateral superior tratado endodonticamente, cuja restauraçäo foi feita com resina composta como material intrarradicular e conformaçäo coronária, em uma única sessäo clínica

Restabelecimento da dimensäo vertical: relato de caso clínico / The recovery of the vertical dimension: clinical case report

Este trabalho relata um caso clínico de perda de dimensäo vertical levando à falência morfológica, funcional e estética. Através de métodos fonéticos, de mensuraçäo facial e fotográficos determinou-se uma dimensäo vertical de oclusäo satisfatória, a qual serviu de ponto de partida para a execuçäo da reabilitaçäo protética do paciente

Fatores que influem na espessura da película de cimentaçäo / Factors affecting cement film thickness

A espessura da película do agente cimentante pode determinar o assentamento incompleto de coroas na fase de cimentaçäo. Assim, os autores fazem uma revisäo dos fatores que afetam a espessura do filme de cimento e apresentam meios de manter essa espessura em níveis aceitáveis, garantindo o resultado final satisfatório da restauraçäo

Anterior esthetic rehabilitation for all-ceramic crowns: a case report / Reabilitação estética anterior para coroas ceramicas: relato de caso

A patient had a serious esthetic problem: one maxillary central incisor was discolored and the other was mal-positioned and fractured. The fabrication of two all-ceramic crowns fulfilled both functional and esthetic objectives

Avaliaçäo da capacidade de cópia de materiais de moldagem elastoméricos de diferentes sistemas por meio de uma técnica aplicável clinicamente / Evaluation of the copying ability of different elastomeric impression materials using a clinically applicable technique

O objetivo deste trabalho foi realizar um estudo comparativo entre diferentes sistemas de materiais de moldagem, tais como o polissulfeto, a silicona de condensaçäo e a silicona de adiçäo, através de uma nova técnica de avaliaçäo näo destrutiva e, conseqüentemente, aplicável clinicamente. A partir da confecçäo de próteses fixas de três elementos, fundidas em liga de níquel-cromo, obtiveram-se réplicas tridimensionais do espaço entre a restauraçäo e o preparo cavitário, utilizando-se uma silicona de condensaçäo. Essas réplicas foram avaliadas microscopicamente. Os resultados indicaram que, embora alguns materiais tenham apresentado comportamento superior, como o Permlastic e o Extrude, os outros materiais estudados tiveram comportamento clinicamente aceitável, desde que seus moldes sejam convenientemente manipulados, principalmente em relaçäo ao tempo de vazamento do gesso

Prótese parcial fixa cantilever anterior: uma ótima opçäo de tratamento / The cantilever fixed partial denture anterior: a good option for tretament

Os autores relatam dois casos clínicos reabilitados com prótese fixa cantilever, para substituiçäo de incisivos lateriais superiores. Este tipo de prótese oferece uma alternativa de tratamento às próteses fixas convencionais, sendo indicada nos dois casos clínicos relatados como uma opçäo de tratamento com o objetivo de preservar tecidos dentais e a estética dos pacientes

Registro interoclusal da relação cêntrica para montagem dos modelos em articulador / Interocclusal reading of the centric relation for mounting of articulator models

Muitos são os métodos e as técnicas para a localização e registro da posição de relação cêntrica. Alguns deles são descritos neste trabalho, que enfoca principalmente a técnica para obtenção de registros precisos da relação cêntrica. O conhecimento e domínio de cada técnica é de suma importância na tentativa de procurar adequá-la aos diferentes casos clínicos